  EFFECT OF SCRAP RATIO ON LIQUID METAL QUALITY OF LOW-PRESSURE DIE-CASTING (LPDC) ALLOY USING ROTARY DEGASSING

  Tokatli, Mehmet; Çolak, Murat; Yüksel, Caglar

  Although various processes are used in aluminum liquid metal cleaning, environmentally friendly, economical and applicable methods should be preferred in industry. Among these methods, the Density Index test based on the reduced pressure test (RPT), which is widely used to measure the efficiency of the rotary degassing process, and the K-mold test method, which offers fast and practical results were carried out. The effects of rotary degassing method on the liquid metal quality of AlSi7Mg0.3 (A356) aluminum alloy charges prepared with different proportions of scrap and ingots were evaluated using a constant 5l/min gas flow rate, a constant 5 min process time and a constant 300 rpm rotor rotation speed. The results show that the Density Index values can be reduced from 1.48% to around 0.74% with increasing scrap rate, while K-mold values can be reduced from 2.8 to 0.6. It was also shown that the rotary degassing method is effective in liquid metal cleaning, and the K-mold test can be used as a very practical control tool for evaluating liquid metal quality.

  • 
  İncele
• MakaleAçık Erişim2024/r/bayburt/16429
  A356 alüminyum alaşımının dökümünde katılaşma zamanı ve Nb ilavesinin mikroyapıya etkisinin incelenmesi

  Colak, Murat; Tokatlı, Mehmet; Yalçın, Önder; Tigli, Ahmet

  Alüminyum alaşımları hafiflik, korozyon direnci, elektrik ve ısı iletkenliğinin yüksek olması yüksek dayanım, sünek olması gibi özelliklerinde dolayı oldukça önemli bir mühendislik malzemesidir. Bu sebeple; otomotiv, havacılık, savunma, uzay endüstrisi, makine imalat, gıda endüstrisi gibi birçok alanda yaygınca kullanım bulmaktadır. Özellikle otomotiv sanayi ve yüksek teknoloji gereksinimi olan birçok sektörde kullanımı artmakla birlikte kalite gereksinimleri de artmaktadır. Alüminyum döküm alaşımlarından kalite beklentisindeki artışa bağlı olarak farklı alaşım elementi ilaveleri ile dökümler yapılması ve üretimde yeni teknoloji kullanımları üzerinde çalışmalar devam etmektedir. Bu çalışmada A356 alüminyum döküm alaşımına %0.03, %0.06 ve %0.1 Niyobyum ilavesinin değişen kesitler içeren kokil kalıba dökümünde mikroyapı üzerindeki etkileri incelenecektir. Çalışmada ergitme, sıvı metal temizleme, kokil kalıba döküm, metalografik numune hazırlama, mikroyapı inceleme ve imaj analiz teknikleri kullanılmıştır. Sonuçlar incelediğinde katılaşma zamanına ve Nb ilave miktarına bağlı olarak döküm mikro yapılarında değişimler olduğu gözlenmiştir.

  AtıfOpenAlex1

  İncele
• MakaleAçık Erişim2023Scopus SJRQ3/r/bayburt/11751
  Correlation Between K-value, Density Index and Bifilm Index in Determination of Liquid Al Cleanliness

  Tigli, A.; Tokatli, M.; Uslu, E.; Colak, M.; Dispinar, D.

  Aluminum alloys are widely used in the industry thanks to its many advantages such as light weight and high strength. The use of this material in the market is increasing day by day with the developing technology. Due to the high energy inputs in the primary production, the use of secondary ingots by recycling from scrap material are more advantageous. However, the liquid metal quality is quite important in the use of secondary aluminum. It is believed that the quality of recycled aluminum is low, for this purpose, many liquid metal cleaning methods and test methods are used in the industry to assess the melt cleanliness level. In this study, it is aimed to examine the liquid metal quality in castings with varying temperature using K mold. A206 alloy was used, and the test parameters were selected as: (i) at 725 °C, 750 °C and 775 °C casting temperatures, (ii) different hydrogen levels. The hydrogen level was adjusted as low, medium and high with degassing, as-cast, and upgassing of the melt, respectively. The liquid metal quality of the cast samples was examined by the K mold technique. When the results were examined, it was determined that metal K values and the number of inclusions were high at the as-cast and up-gas liquid with increasing casting temperatures. It has been understood that the K mold technique is a practical method for the determination of liquid metal quality, if there is no reduced pressure test machine available at the foundry floor.

  AtıfScopus7·WoS6·OpenAlex7

  İncele
• Derleme MakaleYalnız künye2022/r/bayburt/16633
  Alüminyum Alaşımlarının Dökümünde Yaygınca Kullanılan Sıvı Metal Temizleme Yöntemlerinin İncelenmesi

  Yüksel, Çağlar; Colak, Murat; Koşatepe, Abdulhadi; Tokatlı, Mehmet; Saydam, Ferhat; Hal, Murat

  Alüminyum ve alaşımlarının birçok avantajlı özelliği sayesinde metal dökümü endüstrisinde demir-çelikten sonra kendisine ikinci sırada yer bulmayı başarmıştır. Alüminyum üretimi cevherden ve hurdadan geri dönüşüm şeklinde temelde iki farklı prosesle elde edilmektedir. Alüminyumun en önemli hammaddesi boksittir ve birincil alüminyum bu cevherden elde edilir. Alüminyum üretiminde boksit cevherinden üretim, hurdadan geri dönüşüme nazaran çok daha fazla enerjiye ihtiyaç duymaktadır. Üretici girdisinde de ciddi ekonomik değere sahip olan ikincil alüminyum sanayide oldukça fazla kullanılmaktadır. Ancak geri dönüşüm yoluyla ikincil alüminyum kullanımında karşılaşılan en önemli problemler sıvı metal kalitesinin optimizasyonu ve ilave sıvı metal işlemlerinin gereksinimidir. Yüksek kaliteli alüminyum dökümler üretmek için, çözünmüş hidrojenin, çift katlı oksit filmlerinin (bifilm), katışkıların (inklüzyon) ve safsızlıkların (empürite) arındırılması gerekmektedir. Bu amaçla endüstride birçok sıvı metal temizleme yöntemi kullanılmakta ve her geçen gün alternatif yeni yöntemler geliştirme çalışmaları devam etmektedir. Bu derlemede de bu perspektiften bakılarak, alüminyum ve alaşımlarının dökümünde güncel olarak yaygınca kullanım bulan sıvı metal temizleme yöntemlerinden; flaks kullanımı, rotary (döner tip) gaz giderme, kontrollü katılaştırma yöntemi, elektromanyetik yönlü gaz giderme, sprey gaz giderme, ultrasonik gaz giderme yöntemi, vakumlu gaz giderme yöntemleri ele alınmıştır.

  • 