- MakaleAçık Erişim2019Scopus SJRQ3Plasma polymerized linalool (ppLin): An antimicrobial and biocompatible coating
Çakmak, Kenan; Bayram, Özkan; Solak, Kübra; Kaban, Güzin; Şimşek, Önder; Mavi, Ahmet
Bacterial infections in medical devices and drug resistance of bacteria can cause chaos in the world due to loss of lives in addition to the cost of device revisions, quarantine, disinfection of infected areas, and patient treatment. Antibacterial coatings of essential oils on medical devices can prevent bacterial attachment and reduce costs. Linalool is an antibacterial constituent of essential oils. Herein, we examine for the first time the fabrication and characterization of radio frequency (RF) plasma polymerized hydrophilic thin films from linalool (ppLin) by varying deposition parameters (RF power and deposition time) and the behavior of ppLin with two bacteria (Escherichia coli and Staphylococcus aureus) commonly related to microbial contamination of medical devices. While a dramatic reduction in E. coli and S. aureus attachment was observed on ppLin films, their hydrophilic surface was also bactericidal to S. aureus. Additionally, ppLin films were shown to be adherent and noncytotoxic to human fibroblast cells. ppLin can be potentially integrated into medical and other clinical devices as a promising low-cost biocompatible antimicrobial coating.
AtıfScopus8WoS8
İncele - MakaleAçık Erişim2018Scopus SJRQ2A study on the optical, chemical and dielectric properties of PPCIN thin films derived from essential oil compounds using RF plasma polymerisation technique
Bayram, Ozkan; Simsek, Onder
Polymer-based nanostructured films were produced on various substrates using Radio Frequency (RF) plasma polymerization technique from Cinnamaldehyde monomer which is an organic compound. To fabricate polymer thin film, the pressure, the deposition time and RF power were set to 480 mTorr, 30 min and 15, 20 and 30 W, respectively. The effect of RF power on the optical, morphological and chemical properties of thin films were investigated. The optical, morphological and chemical properties were determined by UV–Vis spectroscopy, Atomic Force Microscopy (AFM) and FTIR spectroscopy, respectively. The average surface roughness of thin films was detected as 5.7 nm, 3.9 nm and 11.7 nm using AFM depending on the increase in RF power. Using FTIR spectroscopy, the chemical structure of the polymer thin films was compared with that of the monomer material, and it was found that the majority of the functional groups belonging to the monomers also appeared in the thin films. Optical band gap of thin films increased with RF power and these values were determined as 2.83 eV, 3.05 eV and 2.98 eV, respectively. The extinction coefficients and refractive indices of the thin films were measured at 500 nm between 0.00183–0.00522 and 2.40–2.78, respectively.
AtıfScopus14WoS14OpenAlex16İncele