- MakaleYalnız künye2018Scopus SJRQ2Influence of freeze-thaw on strength of clayey soil stabilized with lime and perlite
Yilmaz, Fatih; Fidan, Duygu
Stabilization of clayey soil has been studied from past to present by mixing different additives to the soil to increase its strength and durability. In recent years, there has been an increasing interest in stabilization of soils with natural pozzolans. Despite this, very few studies have investigated the impact of pozzolanic additives under freeze-thaw cycling. This paper presents the results of an experimental research study on the durability behavior of clayey soils treated with lime and perlite. For this purpose, soil was stabilized with 6% lime content by weight of dry soil (optimum lime ratio of the the soil), perlite was mixed with it in 0%, 5%, 10%, 20%, 25% and 30% proportions. Test specimens were compacted in the laboratory and cured for 7, 28 and 84 days, after which they were tested for unconfined compression tests. In addition to this, they were subjected to 12 closed system freeze-thaw cycles after curing for 28 days. The results show that the addition of perlite as a pozzolanic additive to lime stabilized soil improves the strength and durability. Unconfined compressive strength increases with increased perlite content. The findings indicate that using natural pozzolan which is cheaper than lime, has positive effect in strength and durability of soils and can result cost reduction of stabilization.
AtıfScopus27WoS25OpenAlex15
İncele - MakaleYalnız künye2010Scopus SJRQ2DETERMINATION OF ALKALI-SILICA REACTION EFFECTS OF ZEOLITIC TUFF ADDITION ON THE DIFFERENT AGGREGATES
Gökçe, H. Suleyman; Taban, Saniye; Simsek, Osman
The aim of this study is to determine the alkali-silica reaction (ASR) related characteristics of crushed stones that are produced from rocks of perlite, andesite and limestone when zeolitic tuff (ZT) is used in the mortar mix as cement replacement in different ratios. Accelerated mortar bar experiments in accordance with ASTM C 1260 were carried out on crushed stone aggregate samples to determine the ASR. CEM I 42.5 R type cement was replaced by ZT material in the following ratios: 0, 10, 20, 30 and 40%; in order to investigate the effects of replacement on the ASR pertaining to the aggregate types, 45 mortar bar pieces were produced. The length change values of the samples were measured on the 3, 7, 14, 28, 42, 56 days according to the accelerated mortar bar method. Measured length changes for the control samples on 14(th) day were found to be 0.570% at the level of potentially harmful for perlite, 0.101% at the level of critic for andesite and 0.061% at the level of harmless for limestone. Length changes at the harmful levels were taken under control for perlite at 30 and 40%, for andesite at 20, 30 and 40% ZT replacement ratios. Length change values of all samples decrease as ZT replacement increases. As a result, ZT replacement is effective to suppress the ASR of reactive aggregates.