  Numerical investigation of the Mode I/Mode II fracture behavior of the hybrid composite joints with a hybrid bondline

  Erbayrak, Engin

  In this study, the fracture behavior of fracture characterization bonded joints consisting of hybrid composite adherends and hybrid bondlines under Mode I and Mode II loadings were investigated numerically. Numerical analysis was performed using LS-DYNA. Hybrid composite laminates (HCGFRE) obtained by sequencing plain woven glass fiber reinforced epoxy (GFRE) and plain woven carbon fiber reinforced laminates (CFRE) as adherends. Araldite AV138M and Araldite 2015 epoxy adhesives were also used to create the hybrid bondline. Mode I and mode II fracture behaviors were determined by numerical modeling of the Double Cantilever Beam (DCB) and End Notched Flexural (ENF) tests, respectively. In the numerical model, firstly, the fracture parameters of the relevant adhesives were found in the literature, and verification was made utilizing the numerical model. Then, the fracture behavior in both two modes was examined by forming a hybrid bondline. In the literature, there are restricted studies examining the fracture behavior of fracture characterization bonded joints with hybrid bondlines. Additionally, it is not encountered any study determining the both mode I and mode II fracture behavior of composite fracture characterization bonded joints with hybrid bondlines. Therefore, it is thought that this study will gain significant novelties to the existing literature.

  AtıfScopus1·OpenAlex2

  İncele
• MakaleAçık Erişim2022Scopus SJRQ2/r/bayburt/13568
  Investigations of low-velocity impact behaviour of single-lap joints having dissimilar hybrid composite adherends through cohesive zone model approach

  Erbayrak, Engin

  The low-velocity impact behavior of single-lap joints was investigated in this study. In single-lap joints, woven carbon fiber reinforced epoxy (CFRE) and plain woven glass fiber reinforced epoxy (GFRE) laminates as well as a hybrid composite laminate (HCGFRE), which is formed by stacking carbon and glass composite laminates, are used as adherends. Araldite 2011 and Araldite 138 M/HV998 epoxy adhesives were used with different mechanical properties for joining similar and dissimilar composite adherends. Low-velocity impact tests were carried out with 40 J impact energy. Reaction force-time and impact energy-time graphs were obtained from the experimental study as impact response. In numerical analyses, the damage approach of composite adherend was modeled using composite stress-based failure model (Mat 59) and adhesives were modeled utilizing a mixed-mode cohesive zone model (Mat 138) that existed in LS-DYNA explicit finite element software. It was seen that the numerical results indicated a similar tendency with the experimental results due to the modeling of the adhesives using the proper cohesive zone model, the application of correct boundary conditions, and the selection of the correct contact type.