Yazarlar
Yayınlar
- MakaleAçık Erişim2026Scopus SJRQ3Analysis of the Impact of Blue Stain on the Color, Glossiness, and Whiteness Properties of Scots Pine Lumber
Ayata, Ümit; Peker, Hüseyin; Ulay, Göksel; Çamlıbel, Osman; Atilgan, Abdi
It is known that blue stain causes a loss of price value for Scots pine wood in the wood trade due to the visual defects it creates. In this study, color parameters [red color tone (a*), lightness (L*) value, yellow (b*) color tone, tone angle (h°) value, and chroma (C*) value], whiteness index (WI*) values, and glossiness measurements [at angles of 20°, 60°, and 85°] were compared in Scots pine (Pinus sylvestris L.) wood with normal and blue rot conditions. According to the color parameters obtained, it was determined that the L* value decreased by 11.43%, a* by 79.95%, b* by 28.86%, and C* by 32.75%, while the h° value increased by 17.74%. With the blue coloration, decreases were observed in the 20° glossiness values measured in the ⃦ and ⊥ directions, while increases were observed in the 60° and 85° glossiness values measured in the ⃦ and ⊥ directions. With the blue coloration, decreases of 12.86% in the ⊥ direction and 29.87% in the ⃦ direction in the WI* values were observed. According to these results, it was determined that the wood material with the blue coloration disease had a darker color.
- MakaleAçık Erişim2025Scopus SJRQ3Effect of Thermal Modification and Picture Varnish Application on Color Change of Scots Pine (Pinus Sylvestris L.) Wood
Peker, Hüseyin; Ayata, Ümit; Ulay, Göksel
Scots pine is one of the important tree species used by the wood processing industry in many countries for both interior and exterior applications. It is well known that thermal treatment alters the color of wood. To protect wood from outdoor environmental conditions, certain chemicals are applied to its surface. These protective chemicals also influence the color of thermally treated wood. In this study, the color-altering effect of picture varnish (refined linseed oil), commonly used as a protective chemical in the field of painting, was investigated on both thermally treated and untreated wood materials. Scots pine (Pinus sylvestris L.) wood samples were subjected to thermal treatment at 212 °C for 2 h. Following this, varnish made from refined linseed oil was applied to some of these samples and some untreated samples, with the remaining untreated samples used as controls. Color and whiteness index (WI*) values were analyzed on the resulting four different materials, and the results were compared. Analysis of variance showed significant effects for the factors of heat treatment, picture varnish application, and their interaction, on WI* (|| and ⊥), a*, L*, ho, b*, and C* values. In the non-heat-treated samples, the application of varnish resulted in reductions in WI* values in both directions and in L* values, while increases were observed in ho, b*, C*, and a* values. Additionally, the application of varnish to the heat-treated samples resulted in an increase in a* values, while reductions were observed in WI* values in both directions, as well as in ho, L*, b*, and C* values. After heat treatment, the ∆E* value for Scots pine wood was calculated as 33.63. For both heat-treated and non-heat-treated samples, varnish application resulted in negative ∆L* values and positive ∆a* values. Additionally, ∆b* and ∆C* values were positive in the non-heat-treated and varnished samples, while they were negative in the heat-treated and varnished samples. The protective picture varnish used in the study significantly altered the color of both thermally treated and untreated wood.