- MakaleYalnız künye2019Scopus SJRQ1Vertically oriented graphene nano-sheets grown by plasma enhanced chemical vapor deposition technique at low temperature
Bayram, Ozkan; Simsek, Onder
In this study, it was aimed to obtain vertically-oriented graphene nano-sheets (VGNs) on copper foils using CH 4 gas as the precursor material by means of plasma enhanced chemical vapor deposition (PECVD) technique. VGNs were obtained at 50 W, 75 W and 100 W Radio Frequency (RF) powers by this technique and the effect of RF power on the morphological structure of graphene layers was investigated. VGNs were also analyzed by Raman spectroscopy, scanning electron microscopy (SEM) and water contact angle (WCA) measurements. The SEM images showed that the VGNs became more tightly packed with the increase of RF power and thus these coating parameters had a significant effect on the morphological structure. WCA analyzes for VGNs were also performed and it was found that VGNs obtained at 100 W RF power had higher contact angle value than the other RF powers. These VGNs, which have both large surface area and optically transparent, are thought to be materials that have the potential to be used in supercapacitors and solar cells.
AtıfScopus19WoS17OpenAlex19
İncele - MakaleYalnız künye2019Scopus SJRQ1A study on 3D graphene synthesized directly on Glass/FTO substrates: Its Raman mapping and optical properties
Bayram, Ozkan
In this study, vertically oriented (3D) graphene nanostructures (VGN) were obtained on Glass and Fluorine doped tin oxide (FTO) substrates at relatively low temperatures (approaximatelly at 400 °C) by using plasma enhanced chemical vapor deposition (PECVD) technique. VGNs were characterized using Raman, Uv–Vis and SEM spectroscopies, respectively. Raman spectroscopy showed that growth temperature significantly affected VGN formation and film quality. The layer structures of these VGNs were also confirmed by Raman mapping. The most important data obtained from this study is that although the applied radio frequency (RF) power is the same, the growth temperature significantly affects the graphene formation and morphologies. This was attributed to the fact that CH4 decomposition was very difficult at low temperatures. The optical transmittance of VGNs ranged from 50% to 95% (at 550 nm wavelength) and their electrical conductivity was also determined to be between 5.94 kohm/sqr and 11.2 kohm/sqr. The electrical and optical properties of VGNs, which have a large surface area, indicated that they may be an alternative material for sensor, solar cell and supercapacitor applications.
AtıfScopus19WoS18OpenAlex20İncele