- MakaleAçık Erişim2017Scopus SJRQ1Enhancing the Damping Behavior of Dilute Zn-0.3Al Alloy by Equal Channel Angular Pressing
Demirtas, M.; Atli, K.C.; Yanar, H.; Purcek, G.
The effect of grain size on the damping capacity of a dilute Zn-0.3Al alloy was investigated. It was found that there was a critical strain value (≈1 × 10−4) below and above which damping of Zn-0.3Al showed dynamic and static/dynamic hysteresis behavior, respectively. In the dynamic hysteresis region, damping resulted from viscous sliding of phase/grain boundaries, and decreasing grain size increased the damping capacity. While the quenched sample with 100 to 250 µm grain size showed very limited damping capacity with a loss factor tanδ of less than 0.007, decreasing grain size down to 2 µm by equal channel angular pressing (ECAP) increased tanδ to 0.100 in this region. Dynamic recrystallization due to microplasticity at the sample surface was proposed as the damping mechanism for the first time in the region where the alloy showed the combined aspects of dynamic and static hysteresis damping. In this region, tanδ increased with increasing strain amplitude, and ECAPed sample showed a tanδ value of 0.256 at a strain amplitude of 2 × 10−3, the highest recorded so far in the damping capacity-related studies on ZA alloys.
AtıfScopus8WoS7OpenAlex7
İncele - MakaleYalnız künye2016Scopus SJRQ1Melt Cleanliness Comparison of Chlorine Fluxing and Ar Degassing of Secondary Al-4Cu
Çolak, Murat; Kayikci, Ramazan; Dispinar, Derya
The treatment of liquid aluminum prior to casting typically consists of purging gas and/or fluxes through the melt. By the use of several chemicals during these operations, several environmental problems can occur. Therefore, in this study, the melt cleanliness of Al-4Cu secondary alloy was investigated by comparing the use of argon degassing with or without chlorine fluxing. Reduced pressure test was used to assess the melt quality. Highest quality melt was obtained by Ar degassing with preheated graphite lance without the need to use any chemicals.