Durmuş, Melek; Dispinar, Derya; Gavgali, Mehmet; Uslu, Emin; Çolak, Murat

Elements that are deliberately added to aluminum alloys or are incorporated into the alloy later depending on the production process affect the final product properties. In addition, liquid metal cleaning is important in minimizing undesirable elements. Considering the production process, one of the most harmful impurities that is likely to pass into the alloy via diffusion for aluminum is the element, Fe. It is known that this is due to the fact that although Fe is highly soluble in liquid aluminum and its alloys, it has very little solubility in solids. Depending on the Fe content, mechanical properties, porosity and fluidity properties are affected in aluminum alloys. In this study, stainless and carbon steel rods were dipped into the melt at 700 °C and 750 °C for 1, 2 and 5 h. Castings were performed before and after degassing. Four-channel fluidity mold with different section thickness was used in the trials. Additionally, microstructure characterization was performed under varying casting conditions. Fluidity Index was proposed which is a single value measured from all fluidity values in different sections. When the results were examined, it was determined that the diffusion material, holding time, casting temperature and liquid metal cleanliness had an effect on the fluidity. Due to the increase in diffusion time, a decrease in fluidity was observed in both carbon steel and stainless steel. It was found that fluidity was significantly reduced when using stainless steel.

AtıfScopus14·WoS14·OpenAlex15

İncele

Uslu, Emin; Gavgali, Mehmet; Erdal, Mehmet Okan; Yazman, Şakir; Gemi, Lokman

Fiber-reinforced polymer matrix composites are widely used in many structural applications thanks to their exceptional properties. In recent years, the use of electrospinning nanofibers with unique properties as reinforcement agents has attracted a great deal of attention in improving the performance of these composites. Although there are many promising studies on this subject in the literature, there are still many issues that need to be investigated. In this study, an experimental research reporting on the production and mechanical properties of two-phase polymer matrix composites reinforced with various types of thermoplastic nanofibers is presented. Nanofiber mats were produced from N66, PAN, PVA, and PVC polymers by electrospinning technique. Composites were obtained by embedding these nanofibers into epoxy resin by using vacuum infusion process. Mechanical properties of the composites were determined by performing tensile tests and the results were compared. The morphologies of nanofibers and the fracture surfaces of the composites were examined with SEM. Finally, statistical evaluations were carried out using mechanical data. According to tensile test results, the best ultimate tensile strength of 38.04 ± 3.7 MPa, elongation of 2.46 ± 0.4 % and toughness of 532 ± 137 kJ/m3 were obtained from N66 nanofiber composite, while PVA nanofiber composite was the most favorable in terms of Young's modulus (2.40 GPa). It was observed that the polymer type significantly affected the performance of the composite. In addition to the best mechanical properties, N66 composite was found to be more stable and reproducible than other specimens. Due to the good impregnation of nanofibers, it was conclusively determined that the use of vacuum infusion process is suitable for the production of these materials.

AtıfScopus79·WoS73·OpenAlex81

İncele