Öztürk, Ufuk Kemal; Abderrahmane, Babe Cheikh; Uzun, Oğuzhan; Abdioğlu, Murat; Güner, Sait Barış; Quéval, Loïc

This study introduces a novel Top-Interior Multi-Seeding Melt Growth (TI-MSMG) technique for fabricating high-performance YBCO bulk superconductors and explanations some physical background based on FEM modelling. The depth of the interior seed was gradually changed as 0, 2 and 4 mm (samples S0, S2 and S4, respectively) from the upper surface of the samples. By incorporating an interior seed into the precursor pellet, the TI-MSMG method enables systematic control over grain morphology and critical current density distribution. Magnetic levitation and guidance forces were measured using a three-axis force measurement system, and a two-dimensional finite element method (FEM) model based on the H-formulation of Maxwell’s equations was developed to simulate the electromagnetic behaviour of the superconductors with different seed positions. Experimental and modelling results reveal that samples incorporating an interior seed (S2) exhibit significantly enhanced levitation and guidance forces compared to S0 and S4, attributable to improved inter-domain interactions and morphological consistency, so a better current coupling. The numerical simulations accurately reproduced the experimental findings, confirming the validity of the modelling approach. These findings indicate that the TI-MSMG process not only addresses some limitations of conventional top-seeding methods but also enhances levitation force performance through optimization of interior seed depth, thereby enabling more efficient and tailored designs for high-temperature superconducting systems such as magnetic levitation, energy storage, and superconducting motors.

İncele

Güner, Sait Barış; Abdioğlu, Murat; Öztürk, Kemal; Çelik, Şükrü

In this work, in the first time, we have investigated the levitation and lateral force properties of bulk and cut-pasted bulk GdBCO samples at different temperatures and different cooling heights (CH) to determine the effect of cut-pasted process on the magnetic levitation force behaviour. The measurements of superconducting characteristics indicated that the attractive and repulsive force values of cut-pasted GdBCO sample are slightly lesser than those of GdBCO bulk sample. The maximum repulsive and attractive force values obtained as 15.45 N and −4.56 N for GdBCO bulk and as 14.78 N and −3.92 N for cut-pasted GdBCO samples at 37 K. Although there are many fabrication methods as melt-textured growth (MTG), top seeded infiltration growth (TSIG) and TSMG to produce large HTS samples, the desired large sample size and the sample shape compatible with the superconducting magnetic bearing systems are not still sufficient for the technological applications. In this study, the performed cut-pasted process and obtained magnetic levitation force data can be using for the increment sample size and the desired sample shape in the needed different geometry and size for superconducting magnetic bearing systems.

AtıfScopus8·WoS8·OpenAlex9

İncele