Durmuş, Melek; Dispinar, Derya; Gavgali, Mehmet; Uslu, Emin; Çolak, Murat

Elements that are deliberately added to aluminum alloys or are incorporated into the alloy later depending on the production process affect the final product properties. In addition, liquid metal cleaning is important in minimizing undesirable elements. Considering the production process, one of the most harmful impurities that is likely to pass into the alloy via diffusion for aluminum is the element, Fe. It is known that this is due to the fact that although Fe is highly soluble in liquid aluminum and its alloys, it has very little solubility in solids. Depending on the Fe content, mechanical properties, porosity and fluidity properties are affected in aluminum alloys. In this study, stainless and carbon steel rods were dipped into the melt at 700 °C and 750 °C for 1, 2 and 5 h. Castings were performed before and after degassing. Four-channel fluidity mold with different section thickness was used in the trials. Additionally, microstructure characterization was performed under varying casting conditions. Fluidity Index was proposed which is a single value measured from all fluidity values in different sections. When the results were examined, it was determined that the diffusion material, holding time, casting temperature and liquid metal cleanliness had an effect on the fluidity. Due to the increase in diffusion time, a decrease in fluidity was observed in both carbon steel and stainless steel. It was found that fluidity was significantly reduced when using stainless steel.

AtıfScopus14·WoS14·OpenAlex15

İncele

Colak, Murat; Keskin, Muhammet Emin; Durmuş, Melek; Şekerden, Mete

The casting process involves filling a prepared mould cavity with molten metal, which takes the shape of the container. While the liquid metal takes the shape of the container it is in, the method is attractive, while the volumetric changes during the liquid-solid transformation reveal the importance of moulding design for the manufacture of solid parts. Especially in cast irons, moulds with the same design may produce different results depending on the changing casting and foundry conditions because the volumetric change that occurs during the solidification of ductile cast irons is affected by many parameters and develops differently than in steel and aluminium castings. This study used model wet and resin molding materials to create single and double-riser moulding and castings with different section thicknesses. The importance of the type of mold material used in castings and the number of feeders for the robust production of the cast part was evaluated using experimental and modeling techniques. When the results were examined, it was seen that the shrinkage risk was lower with resin mould than with green sand moulding. In addition, depending on the riser connection point, the importance of the riser neck has emerged.

İncele