Ayata, Umit; Domingos, Idalina; Ferreira, José; Cruz-Lopes, Luísa; Esteves, Bruno

Introduction: This study investigates the Shore-D hardness and surface roughness characteristics of six tropical wood species: Canelo (Nectandra spp.), Limbali (Gibertiodendron dewevrei), Difou (Morus mesozygia), Curupay (Anadenanthera macrocarpa), Ebiara (Berlinia bracteosa), and Zwarte kabbes (Diplotropis martiusii), aiming to assess their suitability for high-performance applications. Objective: To evaluate how wood species and sanding processes influence the mechanical properties and surface quality of selected tropical woods. Methods: Samples were conditioned and sanded using abrasives of different grit sizes (80, 100, 120, 150, and 180). Surface roughness parameters Ra, Rq, and Rz, as well as Shore-D hardness, were measured. Statistical analyses were performed using ANOVA and Duncan’s test. Results: Statistical analysis revealed that abrasive grit size significantly affected surface roughness (p < 0.001), with finer grits producing smoother surfaces. Wood species also had a significant effect on both roughness and hardness. Sanding had the greatest influence on Ra, Rq, and Rz parameters. Ebiara exhibited the smoothest surface, while Curupay showed the highest hardness (74.65). Conclusion: Surface roughness is primarily influenced by sanding grit, whereas hardness is determined by wood species. The results emphasize the importance of tailoring sanding procedures to the wood species in order to optimize surface quality and mechanical performance in industrial and decorative applications.

İncele

Esteves, Bruno; Ayata, Umit; Cruz-Lopes, Luísa; Brás, Isabel; Ferreira, José; Domingos, Idalina

Chemical composition of wood is known to change during thermal treatments. Two species grown in Turkey, afrormosia (Pericopsis elata) and duka (Tapirira guianensis) were heat treated according to Thermowood® method. Lignin, cellulose, hemicelluloses and extractives in dichloromethane, ethanol and water were determined. Wood extracts were analysed by gas chromatography with mass detection and existing compounds were identified by NIST17 database. Results show that hemicelluloses and cellulose content decreased for both heat-treated woods along the treatment while lignin percentage increased. The analysis of extractives has shown several compounds normally associated to lignin thermal degradation that increased along the treatment. At the same time several compounds associated to carbohydrate thermal degradation were found in all the extracts for both heat-treated woods. These founding have allowed the understanding of the degradation pattern of wood during thermal modification. There was not much difference between afrormosia and duka woods structural compounds behaviour along thermal modification. However, the variation of the amount of extractives along the treatment depended on the species.

AtıfScopus20·WoS20·OpenAlex16

İncele