Abdioglu, Murat; Guner, Sait Baris; Ozturk, Kemal; Yang, Chiaming; Chen, Ingann; Celik, Sukru

Although there are studies in literature using different number of seeds with different arrangements, especially line and rectangular, it is seen that there is no detailed study handling the levitation force together with trapped field properties of triangular arrangement of seed in YBCO. Therefore, to further investigate the magnetic properties of seeded YBCO superconductors, we have fabricated cylindrical YBCO (YBa2Cu3O7) superconductors with triangular arrangement of the seeds with different seed distances. Maximum levitation force values were obtained as 39.4 N and 57.1 N, while the maximum guidance force values were obtained as −4.6 N, and −8.7 N, respectively, with single-seeded and triangular-seeded samples with seed distance of 14 mm. It was determined that the trapped field, levitation force, and guidance force firstly decreased from the single-seeded sample to the triangular-seeded sample with small seed distance and then increased with increasing seed distance. Increased field trapping and levitation force performances in the triangular-seeded samples with suitable seed distance indicate that the triangular arrangement of seeds is an eligible method to produce larger dimension YBCO samples with bigger shielding current radius and bigger averaged trapped field values.

AtıfScopus4·WoS4·OpenAlex4

İncele

Abdioglu, Murat; Ozturk, Kemal; Ekici, Mehmet; Savaskan, Burcu; Celik, Sukru; Cansiz, Ahmet

In this article, we have designed and constructed a new multisurface (MS) high temperature superconductor (HTS) Maglev measurement system to investigate the enhancement of magnetic force properties of Maglev systems via MS HTS configurations above conventional permanent magnetic guideway (PMG). We have investigated both the static force and stiffness behavior and dynamic response characteristics of these MS HTS-PMG arrangements in different field cooling heights (FCHs). Optimum cooling height is determined as FCH 20-30 for both six- and four-HTS configurations. The maximum levitation force values of HTS-PMG arrangement with six-HTS were obtained bigger than that of four-HTS in the unit cryostat volume of MS arrangement, indicating that the HTSs at the bottom side of the cryostat make contribution to the loading capacity of Maglev systems. In the present article, it is observed that the magnetic flux density of bottom surface in addition to upper surface of the PMG can make a contribution to loading performance, vertical and lateral stability of Maglev systems. It is thought that the designed measurement facility and results of this study will be beneficial to increase the magnetic flux density in the unit volume via MS HTS-PMG arrangements for future design and construction of the HTS Maglev systems.

AtıfScopus16·WoS6·OpenAlex15

İncele

Erdem, Ozge; Guner, Sait Baris; Celik, Sukru; Kucukomeroglu, Tayfur

This research presents the influence of pyrene (C16H10) addition (0, 2, 4, 6, 8, 10 wt%) on the superconducting properties of bulk MgB2. For C16H10 added MgB2 samples, a shrinkage in a-lattice parameters was determined, whereas c-lattice parameters remained practically unchanged. The (1 1 0) peak observed at 2θ ≈ 59.9◦ slightly shifted to higher angles, the lattice strain increased and the crystallite size reduced after C16H10 addition. By virtue of induced stronger pinning force, the in-field critical current density (Jc) increased after C16H10 addition. The Jc value at 20 K and 4 T was obtained about two times higher (8.54 × 103 A/cm2) for 4 wt% C16H10 added MgB2 sample than that of the pure one. In addition, the variation of levitation force characteristic of MgB2 with increasing C16H10 content was determined at 20, 25 and 30 K. The best vertical levitation force performance in zero-field-cooled regime was obtained as 7.09 N/g at 20 K for 4 wt% C16H10 added MgB2 sample with 13 mm in diameter.

AtıfScopus8·WoS6·OpenAlex8

İncele

Ozturk, Kemal; Abdioglu, Murat; Sahin, Ercin; Celik, Sukru; Gedikli, Hasan; Savaskan, Burcu

In this paper, the levitation force measurements have been carried out by the magnetic force measurement system under both field-cooling and zero-field-cooling regimes, whereas the magnetic field distribution over the permanent-magnet guideway (PMG) was calculated by numerical analysis based on the finite-element method. It was shown in this study that the vertical levitation capability and stability of Maglev systems can be improved depending on the cooling regime, pole number, and suitable arrangement of the PMG. In this paper, it was shown that when the pole number increases, the levitation force density increases. It also appeared that the reasonable position of the supplementary permanent magnet and appropriate cooling heights are key parameters for both levitation performance and stabilization of the high-temperature superconductor (HTS) Maglev. It is believed that the numerical and experimental data in this paper are useful for relative design and practical application of HTS Maglev systems.

AtıfScopus38·WoS33·OpenAlex36